If you’re looking for a transparent optical-grade acrylic for cover glass solutions, then Solaris™ S000 is an excellent choice.
Our Solaris™ solution is industry-leading when it comes to light transmission, low weight, thickness uniformity, and ease of manufacturing processes. This makes it an extremely versatile choice since we can design and manufacture your cover glass and optical filter solution with your exact design and performance requirements.
No Data Found
This data is from a specific batch, and the exact numbers might therefore vary slightly. We therefore assume no responsibility for errors or omissions compared to delivered solutions.
In everything from consumer applications and digital signage to industrial applications and machine vision, our cast acrylic can be customized to optimize the design and performance of your device to match your needs and requirements.
Because of Solaris™’s versatility, it can be improved further by applying surface treatments to either side. These surface treatments range from scratch-, abrasion-, wear resistance, anti-glare, chemical resistance, etc.
Fine Mat and Hard Mat coatings are some of the most common choices for our Solaris™ PMMA range for increased performance and/or durability.
Check out more of our surface treatments in our product selector.
| Parameter | Test | Result |
|---|---|---|
| Light Transmission (Clear) | 450-900nm | ≥ 92% |
| Refractive index | - | 1.49 |
| Parameter | Test | Result |
|---|---|---|
| Tensile strength (rupture) | DIN 53455 | 76 MPa |
| Elongation at rupture | DIN 53455 | 6% |
| Flexural strength (rupture) | DIN 53452 | 130 MPa |
| Compressive strength | DIN 53454 | 130 MPa |
| Impact strength | DIN 53453 | 12 kj/m² |
| Modulus of elasticity | DIN 53455 | 3300 MPa |
| Hardness | ASTM D 785 | 100 |
| Pencil Hardness | ISO 15184 | 3H* |
| Parameter | Test | Result |
|---|---|---|
| Specific heat | ASTM C 351 | 1.32 J/g °C |
| Heat stability - Vicat (3mm) | DIN 53460 | 115 °C |
| Linear thermal exp. coefficient | ASTM D 696 | 0,08 mm/m °C⁻¹ |
| Thermal conductivity | - | 0.17 W/m K |
| Forming temperature | - | 130 to 190 °C |
| Parameter | Test | Result |
|---|---|---|
| Dielectric strength | DIN 53481 | 20-25 kV/mm |
| Volume resistivity | DIN 43482 | 10¹⁵ Ohm cm |
| Dielectric constant | DIN 53483 | 3.7 @ 50 Hz |
| Dielectric constant | DIN 53483 | 2.6 @ 1 MHz |
| Parameter | Test | Result |
|---|---|---|
| Density | DIN 53479 | 1.19 g/cm³ |
| Water absorption | 20 °C for 24 hours | 0.3% |
| Flammability | UL 94 | HB |